| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Certification: | ISO |
| Model Number: | A600 A700 A900 CA70 |
| Minimum Order Quantity: | 1 Ton |
| Price: | USD 400-1000 per Ton |
| Packaging Details: | 25kg bag into jumbo bag |
| Delivery Time: | 5-15 working days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 10000 Ton per month |
| Name: | High Alumina Refractory Cement | Brand: | CA50 A600 A700 A900 CA70 |
|---|---|---|---|
| Color: | Light Yellow | Usage: | Manufacturing Castable And Mixing With High Temperature Products |
| Application: | High Temperature Industrial Furnaces And Kiln | Package: | 3 Layers 25kg Bag Into 2 Layers Jumbo Bag |
| High Light: | 70.5% Al2O3 High Alumina Refractory Cement,68.5% Al2O3 High Alumina Refractory Cement,CA70 fire cement powder |
||
The High Alumina Refractory Cement also well known as calcium aluminate cements, and high alumina castable refractory cement. Generally there are 4 grades of refractory cement according to Al2O3 content and strength, A600, A700,A900 and CA-70. The heat resistance cement can be used for making refractory castable and other high temperature resistant products.
CH Refractories with 500T manufacturing capacity of High Alumina Refractory Cement one day to make sure delivery to customers in time. The refractory aluminum cement will be packaged into three layers 25 kg bag and then into two layers moistureproof polytene jumbo bags directly from the manufacturing line to protect high temp refractory cement from wet air.
As professional manufacturer and company of refractory aluminate cement since 1980, CH refractories company produces and provides customers with a varied range of high-tech calcium aluminate solutions benefiting from the highest performance and quality. The SECAR range offers a large choice of binders based on calcium aluminate technology for fire proof applications. Through its understanding of the customer's needs, CH refractories company has developed one of the widest ranges of aluminate cement for sale on the market.
Physical and chemical index of High Alumina Refractory Cement
| Brand | A600 | A700 | A900 | CA-70 | |
|
Chemical Composition (%)
|
Al2O3 | ≥50 | ≥51 | ≥53.5 | 68.5-70.5 |
| SiO2 | ≤7.8 | ≤7.5 | ≤5.5 | ≤0.5 | |
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ≤0.2 | |
| CaO | / | / | / | 28.5-30.5 | |
| MgO | / | / | / | ≤0.4 | |
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | |
| S | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| Cl | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| 325 mesh residue on sieve(%) | ≤15 | ≤12 | ≤8 | / | |
| d50(μm) | / | / | / | 11-14 | |
| -45μm(%) | / | / | / | ≤8.0 | |
| Specific Surface (m2/kg) | ≥300 | ≥320 | ≥350 | / | |
|
Setting time(h:min)
|
Initial setting (min) | ≥45 | ≥60 | ≥90 | 120-180 |
| Final Setting (min) | ≤6 | ≤6 | ≤6 | 150-240 | |
|
Cold Modulus of Rupture (MPa)
|
24 hour | ≥6 | ≥6.5 | ≥8 | 7.5-10 |
| 72 hour | ≥7 | ≥7.5 | ≥10 | 10-12 | |
|
Cold Crushing Strength (Mpa)
|
24hour | ≥45 | ≥55 | ≥72 | 40-50 |
| 72hour | ≥55 | ≥65 | ≥82 | 45-55 | |
Applications of High Alumina Refractory Cement:
High Alumina Refractory Cement is mainly used to configure refractory castable such as high alumina low cement castable which can build or repair furnace or kiln for heat insulation or high temperature erosion.
Advantages of CH series High Alumina Refractory Cement:
●Fast setting at high temperature
●Increase castable strength
●Can replace castable when using
●Can be added to both heavy and light castable
● Biological acid erosion
● High temperature resistance
●Sulfate corrosion resistance
Manufacturing process of High Alumina Refractory Cement