Place of Origin: | China |
---|---|
Brand Name: | CH Refractories |
Certification: | ISO |
Model Number: | A600 A700 A900 CA70 |
Minimum Order Quantity: | 1 Ton |
Price: | USD 400-1000 per Ton |
Packaging Details: | 25kg bag into jumbo bag |
Delivery Time: | 5-15 working days |
Payment Terms: | L/C, T/T |
Supply Ability: | 10000 Ton per month |
Name: | Calcium Aluminate Cement CA50-A600 A700 A900 | Brand: | A700 A900 CA70 |
---|---|---|---|
Al2O3 Content: | 50-70% | Material: | Alumina Cement |
Refractoriness: | 1700 Degree | Sample: | Avaliable |
Highlight: | 51% Al2O3 Calcium Aluminate Cement,50% Al2O3 Calcium Aluminate Cement,1700c High Aluminous Cement |
The calcium aluminate cements CA50-A600 A700 A900, and high alumina castable refractory cement. Generally there are 4 grades of refractory cement according to Al2O3 content and strength, A600, A700,A900 and CA-70. The heat resistance cement can be used for making refractory castable and other high temperature resistant products.
CH Refractories with 500T manufacturing capacity of High Alumina Refractory Cement one day to make sure delivery to customers in time. The refractory aluminum cement will be packaged into three layers 25 kg bag and then into two layers moistureproof polytene jumbo bags directly from the manufacturing line to protect high temp refractory cement from wet air.
As professional manufacturer and company of refractory aluminate cement since 1980, CH refractories company produces and provides customers with a varied range of high-tech calcium aluminate solutions benefiting from the highest performance and quality. The SECAR range offers a large choice of binders based on calcium aluminate technology for fire proof applications. Through its understanding of the customer's needs, CH refractories company has developed one of the widest ranges of aluminate cement for sale on the market.
The calcium aluminate cements CA50-A600 A700 A900 manufactured by CH Refractories with stable quality and best price. The cement are exported to many countries regularly, such as Saudi, Malaysia, Indonesia and so on. We are waiting for long term cooperation with you
Physical and chemical index of calcium aluminate cements CA50-A600 A700 A900
Brand | A600 | A700 | A900 | CA-70 | |
Chemical Composition (%)
|
Al2O3 | ≥50 | ≥51 | ≥53.5 | 68.5-70.5 |
SiO2 | ≤7.8 | ≤7.5 | ≤5.5 | ≤0.5 | |
Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ≤0.2 | |
CaO | / | / | / | 28.5-30.5 | |
MgO | / | / | / | ≤0.4 | |
R2O | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | |
S | ≤0.1 | ≤0.1 | ≤0.1 | / | |
Cl | ≤0.1 | ≤0.1 | ≤0.1 | / | |
325 mesh residue on sieve(%) | ≤15 | ≤12 | ≤8 | / | |
d50(μm) | / | / | / | 11-14 | |
-45μm(%) | / | / | / | ≤8.0 | |
Specific Surface (m2/kg) | ≥300 | ≥320 | ≥350 | / | |
Setting time(h:min)
|
Initial setting (min) | ≥45 | ≥60 | ≥90 | 120-180 |
Final Setting (min) | ≤6 | ≤6 | ≤6 | 150-240 | |
Cold Modulus of Rupture (MPa)
|
24 hour | ≥6 | ≥6.5 | ≥8 | 7.5-10 |
72 hour | ≥7 | ≥7.5 | ≥10 | 10-12 | |
Cold Crushing Strength (Mpa)
|
24hour | ≥45 | ≥55 | ≥72 | 40-50 |
72hour | ≥55 | ≥65 | ≥82 | 45-55 |
Advantages of CH calcium aluminate cements CA50-A600 A700 A900:
●Fast setting at high temperature
●Increase castable strength
●Can replace castable when using
●Can be added to both heavy and light castable
● Biological acid erosion
● High temperature resistance
●Sulfate corrosion resistance