| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Certification: | ISO |
| Model Number: | CH-N |
| Minimum Order Quantity: | 1 Ton |
| Price: | 200-300 USD/T |
| Packaging Details: | Pallet |
| Delivery Time: | 5-15 working days |
| Payment Terms: | T/T, L/C |
| Supply Ability: | 5000 Ton per month |
| Name: | Hard Fire Brick | Size: | 230*114*65mm |
|---|---|---|---|
| Material: | Alumina Block | Raw Material: | High Alumina Bauxite |
| Refractoriness: | 1580 Degree Min | Bulk Density: | 1.9-2.15g/cm3 |
| High Light: | 230*114*65mm Fire Refractory Bricks,1580C Fire Refractory Bricks,230*114*65mm Heat Proof Bricks |
||
Kiln refractory Hard Fire Brick is made from clinker clay by mixing, forming, drying, sintering and machine pressing moulding with good resistance to corrosion and abrasion, good thermal shock resistance, good spelling resistance, high mechanical strength, good volume stability under high temperature.
The mineral composition of heavy dense Hard Fire Brick mainly is kaolinite(Al2O32SiO22H2O) and 6%~7% impurities (oxides of potassium, sodium, calcium, titanium and iron). The firing process of blast furnace refractory tiles is mainly due to the continuous dehydration of kaolinite to form crystallization of mullite (3Al2O32SiO2). SiO2 and Al2O3 in the yellow fire clay bricks form a eutectic low-melting silicate with impurities during the firing process, surrounding the mullite crystal.
Hard Fire Brick maufactured by CH refractories is made from high quality bauxite,and make sure alumina content and bulk density. We only provide stable quality product.
Hard Fire Brick is one of the most widely used fire brick, which need large quantity, so price is important for customer. We will provide most competitive price for all of the customers. Our bricks has been widely imported to many countires, such as Malaysia, Indonesia, Pakistan and so on. Welcome to ask price directly.
| Items | Index of Hard Fire Brick | ||||||||
| / | CH-N-1 | CH-N2a | CH-N-2b | CH-N-3a | CH-N-3b | CH-N-4 | CH-N-5 | CH-N-6 | |
| Refractoriness /℃≥ | 1750 | 1730 | 1730 | 1710 | 1710 | 1690 | 1670 | 1580 | |
| 0.2Mpa Refractoriness under load(RUL)/℃≥ | 1400 | 1350 | 1320 | 1300 | |||||
| Reheating linear change/℃(1500℃,2h) | 1400℃2h | +0.1 -0.4 | +0.1 -0.5 | +0.2 -0.5 | |||||
| 1350℃2h | +0.2-0.5 | +0.2-0.5 | +0.2-0.5 | +0.2-0.5 | |||||
| Apparent porosity/% ≤ | 22 | 24 | 26 | 24 | 26 | 24 | 26 | 28 | |
| CCS/Mpa ≥ | 30 | 25 | 20 | 15 | 15 | 20 | 15 | 15 | |
Applications of Clay Fire Bricks :
Fire Clay Brick plays an incomparable important role in the development of high temperature industrial kiln production, which is the indispensable basic alumina heat resistant material to ensure following production running and technological development.
Fire Clay Brick can be applied to
Machinery and boiler
Steel and nonferrous metals
Glass, cement and ceramics
Light industry and electric power
War industry and other economic filed