High Strength 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Slag Resistance

Basic Information
Place of Origin: China
Brand Name: CH Refractories
Certification: ISO
Model Number: LCC
Minimum Order Quantity: 1 Ton
Price: USD 200-1000 per Ton
Packaging Details: 25kg bag into jumbo bag
Delivery Time: 5-15 working days
Payment Terms: L/C, T/T
Supply Ability: 5000 Ton per month
Detail Information
Name: LCC Low Cement Castable Al2o3 Content (%): 65-85% Or Customized
Usage: Industrial Furnaces, Rotary Furnace, Cement Kiln, Waster Incineration Furnace, Tundish Or Other Heating Furnace Type: Fire Resistance Castable
Material: Alumina Castable Bulk Density: 3.0-3.5g/cm3
High Light:

LCC Low Cement Castable

,

1600 Degree Low Cement Castable

,

85% low cement refractory castable


Product Description

High Strength Slag Resistance 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Castable

LCC Low Cement Castable

 

LCC Low cement refractory castable made by CH Refractories with three levels, which are high aluminum low cement castable, mullite low cement castable and corundum low cement castable. The low cement fireproof castable is mainly used for cement kiln masonryespecially for kiln mouth, kiln door cover, cooler, tertiary air duct and coal injection pipe.
The LCC low cement castable made by CH Refractories can be made into fast drying explosion-proof castable according to baking time requirements, which has following advantages comparing with common refractory castable:
. The water consumption is less, only 1/2-1/3(about 5-7%) of common refractory castables, so the bulk density is high, the porosity is low, no obvious dehydration stage when baking, and the thermal shock performance is good, which is comparable to the sintered products.
. The high temperature performance and slag resistance of the material are improved compare with common refractory castable, because the amount of cement is greatly reduced,
. After curing, there are few hydrates or anhydrous compounds, and no hydration bond is destroyed during baking, which affects the medium temperature strength or high temperature strength.

Items High aluminum Mullite Corundum
/ CH-LCC65 CH-LCC70 CH-LCC85
AL2O3% 65 70 85
Bulk density (110℃×24h) g/cm3 2.5 2.6 2.8
Flexural strength/ MPa ≥ 110℃×24h 10 11 12
1400℃×3h 12 13 14
Compressive strength/MPa ≥ 110℃×24h 80 90 100
1400℃×3h 90 90 100
PLC(1400℃×3h)/ % 0.5 0.5 0.5
Maximum Service temperature/℃ 1500 1550 1600

 


Advantages of LCC Low Cement Castable:
Higher strength than common castable
Made from high quality raw material
Excellent strength at various temperatures
Good thermal shock resistance

 

Package and delivery of LCC Low Cement Castable:

High Strength 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Slag Resistance 0
High Strength 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Slag Resistance 1
High Strength 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Slag Resistance 2
 
 
 