Name: Secar 71 high temp refractory cement Castable Binder High Temperature Resistant
Brand: Secar
SKU: Secar 71
Price: 1000 USD
Availability: InStock
Rating: 4.8 (157 reviews)

Secar 71 high temp refractory cement Castable Binder High Temperature Resistant

Place of Origin:

China

Brand Name:

Secar

Certification:

ISO

Model Number:

Secar 71

Minimum Order Quantity:

1 Ton

Price:

FOB 1000-1200 USD/T

Packaging Details:

25kg bag into jumbo bag

Delivery Time:

5-15 working days

Payment Terms:

L/C, T/T

Supply Ability:

5000 Ton per month

Name:

Refractory Cement Secar 71

Al2o3 Content (%):

70%

Application:

Refractory Castables

Color:

White

Sample:

Refractory Cement Free Sample

Usage:

Fire Resistance Place

High Light:

Secar 71 High Temp Refractory Cement

70% High Temp Refractory Cement

Secar 68 refractory concrete mix

Refractory cement Secar 71

General Characteristics of Refractory cement Secar 71

SECAR® 71 is a versatile hydraulic binder with an alumina content of approximately 70%, which is designed to be used at temperatures in excess of1400°C.

SECAR® 71, a pure cement manufactured by the sintering process, contains only calcium aluminates. The high calcium aluminate content provides characteristics ideally suited for refractory applications where rapid hardening combined with excellent mechanical resistance and high temperature performance are required.

Using SECAR® 71 as a refractory cement normally finds it as the primary binder in mortars and concretes exposed to refractory temperatures. SECAR® 71 is preferred by many for high duty refractory concretes due to a very low iron oxide content of approximately 0.1%.

SECAR® 71 is the reference product for high technology deflocculated castable systems such as LCC, ULCC, shotcrete and pumpable refractories. Its controlled mineralogy gives the formulator great flexibility in castable design and also gives good compatibility with micro silica.

Specifications of Refractory cement Secar 71

Chemical constituents (% by XRF chemistry)

Al2O3

CaO

SiO2

Fe2O3

≥68.5

≥ 31.0

≥ 0.8

≥ 0.4

Blaine fineness: 3700-4500 cm2/g (ASTM C204)

Physical Properties (using EN-196 sand mortar)

 Flow at 30 min:  60% (ASTM C1437)

 Vicat Initial Set:  175 min.

 Vicat Final Set:  290 min

Modified ASTM C191 - Needle weight is 1000g, needle diameter

is 1.16 mm, samples immersed in water.

 Compressive strength (ASTM C349)

6 hr  1250 psi (8.6 MPa)

24 hr  4600 psi (31.7 MPa)

CH Refractories is cooperating with Chinese Secar agent, can supply you Secar cement with competitive price. If you need Secar cement, welcome to ask price.

Packaging & Shelf Life

SECAR® 71 is available palletized in 50 lb bags, 100 lb bags or 3000 lb. super sacks.

SECAR® 71 packaging is designed to protect it from humidity. However, as with all hydraulic binders, it is recommended that SECAR® 71 not be placed outdoors or in direct contact with the ground. When correctly stored in dry conditions, the properties of SECAR® 71

will remain within specification limit for at least 6 months. In most cases, its properties will be retained for over a year.

$Secar 71 high temp refractory cement Castable Binder High Temperature Resistant 0$

$Secar 71 high temp refractory cement Castable Binder High Temperature Resistant 1$

$Secar 71 high temp refractory cement Castable Binder High Temperature Resistant 2$

$70.5% High Alumina Refractory Cement$

Secar 71 high temp refractory cement Castable Binder High Temperature Resistant

Secar 71 High Temp Refractory Cement

70% High Temp Refractory Cement

Secar 68 refractory concrete mix

Refractory cement Secar 71 castable binder high temperature resistant

Refractory cement Secar 71

70.5% High Alumina Refractory Cement,

53.5% High Alumina Refractory Cement,

51% calcium sulphoaluminate cement

70.5% High Alumina Refractory Cement

CA50 A700 High Alumina Refractory Cement

A600 Refractory Cement Powder

1700 Degree Refractoriness High Combination Alumina Cement With High Strength

2mm High Alumina Refractory Concrete Particle Size 70% Al2O3 Composition 1.2W/M.K

25kg/Bag High Alumina Refractory Cement 2mm High Strength With Good Flowability

HAC Cement For High Temperature Furnace And Kiln Softening Point ≥1300℃

A900 High Alumina Refractory Cement 1700 Degree Refractoriness Al2O3≥70% 2mm