Name: Secar 71 Secar 68 Calcium Sulphoaluminate Cement Primary Binder
Brand: Secar
SKU: Secar 71 & Secar 68
Price: 1000 USD
Availability: InStock
Rating: 4.5 (120 reviews)

Secar 71 Secar 68 Calcium Sulphoaluminate Cement Primary Binder

Basic Information

Place of Origin:	China
Brand Name:	Secar
Certification:	ISO
Model Number:	Secar 71 & Secar 68

Minimum Order Quantity:	1 Ton
Price:	FOB 1000-1200 USD/T
Packaging Details:	25kg bag into jumbo bag
Delivery Time:	5-15 working days
Payment Terms:	L/C, T/T
Supply Ability:	5000 Ton per month

Get Best Price Contact Now

Name:

Calcium Aluminate Cement

Fe2o3:

Approximately 0.1%

Type:

Cement Refractory Cement

Usage:

Castable Or Mortar Manufacturing

Advantage:

Good Flowability

Package:

5 Layers Bags

High Light:

Secar 68 Calcium Sulphoaluminate Cement

Secar 71 Calcium Sulphoaluminate Cement

Primary Binder secar 71 cement

Calcium Aluminate Cement

General Characteristics of Refractory cement Secar 71

SECAR® 71 is a versatile hydraulic binder with an alumina content of approximately 70%, which is designed to be used at temperatures in excess of1400°C.

SECAR® 71, a pure cement manufactured by the sintering process, contains only calcium aluminates. The high calcium aluminate content provides characteristics ideally suited for refractory applications where rapid hardening combined with excellent mechanical resistance and high temperature performance are required.

SECAR® 71 is the reference product for high technology deflocculated castable systems such as LCC, ULCC, shotcrete and pumpable refractories. Its controlled mineralogy gives the formulator great flexibility in castable design and also gives good

compatibility with micro silica.

Calcium aluminate cements do not release Calcium Hydroxide as a hydration product when used as the sole hydraulic compound in a formulation. This imparts good refractoriness and chemical resistance.

Specifications of Refractory cement Secar 71

Chemical constituents (% by XRF chemistry)

Al2O3

CaO

SiO2

Fe2O3

≥68.5

≥ 31.0

≥ 0.8

≥ 0.4

Blaine fineness: 3700-4500 cm2/g (ASTM C204)

Physical Properties (using EN-196 sand mortar)

 Flow at 30 min:  60% (ASTM C1437)

 Vicat Initial Set:  175 min.

 Vicat Final Set:  290 min

Modified ASTM C191 - Needle weight is 1000g, needle diameter

is 1.16 mm, samples immersed in water.

 Compressive strength (ASTM C349)

6 hr  1250 psi (8.6 MPa)

24 hr  4600 psi (31.7 MPa)

CH Refractories is cooperating with Chinese Secar agent, can supply you Secar cement with competitive price. If you need Secar cement, welcome to ask price.

Packaging & Shelf Life

SECAR® 71 is available palletized in 50 lb bags, 100 lb bags or 3000 lb. super sacks.

SECAR® 71 packaging is designed to protect it from humidity. However, as with all hydraulic binders, it is recommended that SECAR® 71 not be placed outdoors or in direct contact with the ground. When correctly stored in dry conditions, the properties of SECAR® 71

will remain within specification limit for at least 6 months. In most cases, its properties will be retained for over a year.

$70.5% High Alumina Refractory Cement$

Secar 71 Secar 68 Calcium Sulphoaluminate Cement Primary Binder

Secar 68 Calcium Sulphoaluminate Cement

Secar 71 Calcium Sulphoaluminate Cement

Primary Binder secar 71 cement

The Primary Binder In Mortars And Concretes Secar 71 Secar 68 Calcium Aluminate Cement

Calcium Aluminate Cement

70.5% High Alumina Refractory Cement,

53.5% High Alumina Refractory Cement,

51% calcium sulphoaluminate cement

70.5% High Alumina Refractory Cement

CA50 A700 High Alumina Refractory Cement

A600 Refractory Cement Powder

1700 Degree Refractoriness High Combination Alumina Cement With High Strength

2mm High Alumina Refractory Concrete Particle Size 70% Al2O3 Composition 1.2W/M.K

25kg/Bag High Alumina Refractory Cement 2mm High Strength With Good Flowability

HAC Cement For High Temperature Furnace And Kiln Softening Point ≥1300℃

A900 High Alumina Refractory Cement 1700 Degree Refractoriness Al2O3≥70% 2mm