| Name: | Refractory Cement Powder | Brand: | CA50-A600 A700 A900 |
|---|---|---|---|
| Al2O3 Content: | 50-70% Or As Requirements | Raw Material: | High Alumina Bauxite |
| Fe2o3: | ≤2.5 | Usage: | Fire Resistance Place |
| High Light: | A900 Refractory Cement Powder,A700 Refractory Cement Powder,70% castable refractory mix |
||
The Refractory Cement Powder CA50-A600 A700 A900, also called as cement refractory castable cement. Generally there are 4 grades of refractory cement according to Al2O3 content and strength, A600, A700,A900 and CA-70. The heat resistance cement can be used for making refractory castable and other high temperature resistant products.
CH Refractories with 500T manufacturing capacity of High Alumina Refractory Cement one day to make sure delivery to customers in time.
As professional manufacturer and company of refractory aluminate cement since 1980, CH refractories company produces and provides customers with a varied range of high-tech calcium aluminate solutions benefiting from the highest performance and quality. The SECAR range offers a large choice of binders based on calcium aluminate technology for fire proof applications. Through its understanding of the customer's needs, CH refractories company has developed one of the widest ranges of aluminate cement for sale on the market.
The calcium aluminate cements CA50-A600 A700 A900 manufactured by CH Refractories with stable quality and best price. The cement are exported to many countries regularly, such as Saudi, Malaysia, Indonesia and so on. We are waiting for long term cooperation with you
Physical and chemical index of calcium aluminate cements CA50-A600 A700 A900
| Brand | A600 | A700 | A900 | CA-70 | |
|
Chemical Composition (%)
|
Al2O3 | ≥50 | ≥51 | ≥53.5 | 68.5-70.5 |
| SiO2 | ≤7.8 | ≤7.5 | ≤5.5 | ≤0.5 | |
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ≤0.2 | |
| CaO | / | / | / | 28.5-30.5 | |
| MgO | / | / | / | ≤0.4 | |
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | |
| S | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| Cl | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| 325 mesh residue on sieve(%) | ≤15 | ≤12 | ≤8 | / | |
| d50(μm) | / | / | / | 11-14 | |
| -45μm(%) | / | / | / | ≤8.0 | |
| Specific Surface (m2/kg) | ≥300 | ≥320 | ≥350 | / | |
|
Setting time(h:min)
|
Initial setting (min) | ≥45 | ≥60 | ≥90 | 120-180 |
| Final Setting (min) | ≤6 | ≤6 | ≤6 | 150-240 | |
|
Cold Modulus of Rupture (MPa)
|
24 hour | ≥6 | ≥6.5 | ≥8 | 7.5-10 |
| 72 hour | ≥7 | ≥7.5 | ≥10 | 10-12 | |
|
Cold Crushing Strength (Mpa)
|
24hour | ≥45 | ≥55 | ≥72 | 40-50 |
| 72hour | ≥55 | ≥65 | ≥82 | 45-55 | |