| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Certification: | ISO |
| Model Number: | A600 A700 A900 CA70 |
| Minimum Order Quantity: | 1 Ton |
| Price: | USD 400-1000 per Ton |
| Packaging Details: | 25kg bag into jumbo bag |
| Delivery Time: | 5-15 working days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 10000 Ton per month |
| Name: | High Temperature Calcium Aluminate Cement CA50-A700 Refractory | Type: | Cement Refractory Cement |
|---|---|---|---|
| Advantage: | High Wear Resistance | Usage: | Fire Resistance Place |
| Material: | CaO·Al2O3 | Color: | Light Brown |
| Highlight: | 70.5% High Alumina Refractory Cement,53.5% High Alumina Refractory Cement,51% calcium sulphoaluminate cement |
||
High Temperature Calcium Aluminate Cement CA50-A700 Refractory
The calcium aluminate cements CA50-A600 A700 A900, and high alumina castable refractory cement. Generally there are 4 grades of refractory cement according to Al2O3 content and strength, A600, A700,A900 and CA-70.
Calcium aluminate cement is mainly used as a binder for refractory castables and ejectors. Clay, high aluminum castable use common calcium aluminate cement as binder, rigid jade, mullite, chromium containing rigid jade, spinel castable use pure calcium aluminate cement as binder.
CH Refractories with 500T manufacturing capacity of High Alumina Refractory Cement one day to make sure delivery to customers in time. The refractory aluminum cement will be packaged into three layers 25 kg bag and then into two layers moistureproof polytene jumbo bags directly from the manufacturing line to protect high temp refractory cement from wet air.
The calcium aluminate cements CA50-A600 A700 A900 manufactured by CH Refractories with stable quality and best price. The cement are exported to many countries regularly, such as Saudi, Malaysia, Indonesia and so on. We are waiting for long term cooperation with you.
Physical and chemical index of calcium aluminate cements CA50-A600 A700 A900
| Brand | A600 | A700 | A900 | CA-70 | |
|
Chemical Composition (%)
|
Al2O3 | ≥50 | ≥51 | ≥53.5 | 68.5-70.5 |
| SiO2 | ≤7.8 | ≤7.5 | ≤5.5 | ≤0.5 | |
| Fe2O3 | ≤2.5 | ≤2.5 | ≤2.5 | ≤0.2 | |
| CaO | / | / | / | 28.5-30.5 | |
| MgO | / | / | / | ≤0.4 | |
| R2O | ≤0.4 | ≤0.4 | ≤0.4 | ≤0.4 | |
| S | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| Cl | ≤0.1 | ≤0.1 | ≤0.1 | / | |
| 325 mesh residue on sieve(%) | ≤15 | ≤12 | ≤8 | / | |
| d50(μm) | / | / | / | 11-14 | |
| -45μm(%) | / | / | / | ≤8.0 | |
| Specific Surface (m2/kg) | ≥300 | ≥320 | ≥350 | / | |
|
Setting time(h:min)
|
Initial setting (min) | ≥45 | ≥60 | ≥90 | 120-180 |
| Final Setting (min) | ≤6 | ≤6 | ≤6 | 150-240 | |
|
Cold Modulus of Rupture (MPa)
|
24 hour | ≥6 | ≥6.5 | ≥8 | 7.5-10 |
| 72 hour | ≥7 | ≥7.5 | ≥10 | 10-12 | |
|
Cold Crushing Strength (Mpa)
|
24hour | ≥45 | ≥55 | ≥72 | 40-50 |
| 72hour | ≥55 | ≥65 | ≥82 | 45-55 | |
Advantages of CH calcium aluminate cements CA50-A600 A700 A900:
●Fast setting at high temperature
●Increase castable strength
●Can replace castable when using
●Can be added to both heavy and light castable
● Biological acid erosion
● High temperature resistance
●Sulfate corrosion resistance