|Name:||Nonferrous Metal Applied Sintered Magnesia Chrome Brick||Shape:||Standard Or Special Shape|
|Feature:||Good Refractoriness Degree||Application:||Nonferrous Metal Melting|
|Bulk Density:||3.2-3.38g/cm3||Usage:||Nonferrous Metal Melting Furnace|
Sintered Magnesia Chrome Brick,
Refining Furnace Magnesia Chrome Brick,
Metal Melting magnesite chrome brick
Nonferrous Metal melting Applied Sintered Magnesia Chrome Brick For Refining Furnace, Rotary Kiln
The refractory magnesia chrome refractory brick is a product made of high-purity magnesia and imported chrome concentrate, which is made by adding a small amount of additives and high pressure and high temperature. Generally there are three different magnesia chrome refractory bricks according to manufacturing method, which are:
1.Common magnesite chrome refractory brick is made by sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate.
2.Direct-bonded magnesite chrome refractory brick is made by chrome ore with low content of impurities and pure magnesite,firing at the temperature above 1700°C.
3.Semi-rebonded and fuse-rebonded magnesite chrome refractory brick are made by fused magnesite chrome sinter.
|Apparent porosity/% ≤||15||16||15||16||15||16||15||16||15||16||15||16|
|Bulk density g/cm3||3.38||3.38||3.33||3.33||3.30||3.30||3.25||3.25||3.20||3.20||3.20|
CH Refractories has been major in refractories manufacturing for three decades year, our professional engineers will suggest you the most suitable and economical magnesia chrome refractory brick according to your kiln or furnace casting condition to save your money and achieve the best performance.
Photos of Nonferrous Metal Applied Sintered Magnesia Chrome Brick
Package of Sintered Magnesia Chrome Brick