| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Certification: | ISO |
| Model Number: | MZ |
| Minimum Order Quantity: | 1 Ton |
| Price: | USD 400-1000 per Ton |
| Packaging Details: | Pallet |
| Delivery Time: | 5-15 working days |
| Payment Terms: | T/T, L/C |
| Supply Ability: | 10000 Ton per month |
| Name: | High Strength Magnesia Bricks | Application: | EAF, Converter Furnace Of Steel Making |
|---|---|---|---|
| Mgo Content (%): | 90%~97% | Bulk Density: | 2.85~2.9/gcm3 |
| Shape: | Brick | Type: | Factory |
| High Light: | 97% Magnesia Fire Rated Bricks,90% Magnesia Fire Rated Bricks,97% Mgo Fire Retardant Bricks |
||
High Strength Magnesia Bricks Fire Rated Bricks Fire Retardant Bricks
High-quality Dead Burned Magnesia Refractory Brick is a product made of high-grade molding and high-temperature firing using first-grade magnesia and high-purity magnesia as raw materials. Dead Burned Magnesia Refractory Brick has excellent heat resistant and high resistance to alkali slag erosion.
It is mainly used for basic open hearth furnace, electric furnace bottom and wall, permanent lining of oxygen converter, non-ferrous metal smelting furnace, high temperature tunnel kiln, calcined magnesia brick and lining of cement rotary kiln, furnace bottom and wall of heating furnace, lattice brick of regenerative chamber of glass kiln, etc.
| Items | CH-MZ-91 | CH-MZ-93 | CH-MZ-95 | CH-MZ-97 |
| Mgo% ≥ | 90 | 93 | 95 | 97 |
| SiO2%≤ | -- | -- | 2.50 | 1.20 |
| CaO%≤ | 3.0 | 2.50 | 2.0 | 1.50 |
| Apparent porosity/%≤ | 20 | 18 | 18 | 18 |
| CCS /MPa ≥ | 40 | 50 | 50 | 50 |
| 0.2 MPa Refractoriness Under Load/℃ | 1500 | 1550 | 1600 | 1650 |
Applications of Fused Magnesium Bricks :
●Glass Industry glass furnace regenerator checker
●Building field
●lime kiln,cement kiln
●Refractory field
●Calcination kiln,shaft kiln and tunnel kiln
●Non-ferrous metallurgical field
●Converter furnace and EAF
●Copper,nickel,lead,zinc,tin smelting furnace lining, refined copper
Features of CH Series magnesia refractory brick
Higher temperate resistant with good refractoriness
Good performance in high temp refractoriness under load
Excellent resistance in slag abrasion
Higher bulk density
Lower apparent porosity
Lower impurity content