| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Certification: | ISO |
| Model Number: | CHCB93 |
| Minimum Order Quantity: | 1 Ton |
| Price: | 800USD/MT |
| Packaging Details: | Pallet |
| Delivery Time: | 20-30days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 1000/MT/Month |
| Shape: : | Brick | Company type: : | Factory |
|---|---|---|---|
| Brand: : | CH Refractories | Certificate: : | ISO9001 |
| Highlight: | High Alumina Chrome Brick,Alumina Chrome Brick With Heat Shock,Chemical Industry Kiln Alumina Chrome Brick |
||
High Alumina Chrome Brick With Heat Shock For Chemical Industry Kiln
At present, the application of aluminum chrome brick has been more widely used, one is made of metal chromium slag as the main raw material of chromium corundum brick, the product is widely used in zinc smelting furnace, volatile kiln, chromium corundum brick has excellent thermal vibration stability and high temperature creep performance, and meet the requirements of national circular economy.
The chrome corundum brick products I produce are made of corundum and fused chromium oxide as the main raw materials, with micro powder and other additives, after mixing, forming, drying, and firing at high temperature in shuttle kiln. Products with wear resistance, heat shock, acid and alkali erosion and other characteristics. High chromium brick (Cr2O3≥90%) is mainly used in coal chemical industry, chemical industry kiln, alkali free glass fiber kiln, garbage incinerator and other key parts of kiln;
Chrome corundum brick is mainly used in the lining of carbon black furnace, copper smelting furnace, glass furnace melting pool, steel rolling furnace slide, steel platform. Product size, physical and chemical indicators, service life has reached or exceeded the level of similar products at home and abroad.
Specification:
| Item | High chromium oxide brick | Medium chrome oxide brick | chrome corundum brick | chrome corundum brick | chrome corundum brick |
| Cr2O3 % | ≥93 | ≥86 | ≥60 | ≥30 | ≥12 |
| Al2O3 % | — | — | ≤38 | ≤68 | ≤80 |
| Fe2O3 % | — | — | ≤0.2 | ≤0.2 | ≤0.5 |
| Appearance porosity % | ≤17 | ≤17 | ≤14 | ≤16 | ≤18 |
| Bulk density g/cm3 | ≥4.3 | ≥4.2 | ≥3.63 | ≥3.53 | ≥3.3 |
| Cold crushing strength MPa | ≥100 | ≥100 | ≥130 | ≥130 | ≥120 |
| Refractoriness under load℃(0.2Mpa,0.6%) | ≥1680 | ≥1670 | ≥1700 | ≥1700 | ≥1700 |
| Linear change on reheating % | ±0.2 | ±0.2 | ±0.2 | ±0.2 | ±0.2 |