| Place of Origin: | China |
|---|---|
| Brand Name: | CH Refractories |
| Model Number: | CH-N |
| Bulk Density: | 2.7-3.0 G/cm3 | Corrosion Resistance: | Good |
|---|---|---|---|
| Linear Change: | ≤0.4% | Thermal Expansion Coefficient: | 2.5-3.5×10-6/℃ |
| Apparent Porosity: | ≤18% | Refractoriness: | 1700-1800℃ |
| Chemical Composition: | MgO-Cr2O3 | Thermal Conductivity: | ≤0.7 W/m.k |
| Highlight: | High Cold Crushing Strength Mgo Bricks,2.7 G/cm3 Mgo Bricks,Industrial Use Mgo Chrome Bricks |
||
Magnesia Chrome Brick is a kind of magnesite chrome refractory brick made of magnesia and chrome oxide as the main raw materials, through firing and forming. It has excellent properties such as high temperature resistance, thermal shock resistance, wear resistance, good thermal insulation, high refractoriness, low iron content, good stability, and high bulk density. The typical physical and chemical properties of Magnesia Chrome Bricks include bulk density of 2.7-3.0 g/cm3, thermal conductivity ≤0.7 w/m.k, thermal expansion coefficient of 2.5-3.5×10-6/℃, linear change ≤0.4%, and cold crushing strength ≥50 MPa. Magnesia Chrome Brick is widely used in various high temperature industrial furnaces and kilns due to its excellent properties, such as magnesite chrome kiln, mgo bricks for glass kiln, magnesia refractory bricks for electric arc furnace, and mgo refractory bricks for steel ladle.
| Name | Value |
|---|---|
| Thermal Expansion Coefficient | 2.5-3.5×10-6/℃ |
| Mohs Hardness | 7.5-8.5 |
| Thermal Conductivity | ≤0.7 W/m.k |
| Cold Crushing Strength | ≥50 MPa |
| Chemical Composition | MgO-Cr2O3 |
| Porosity | ≤22% |
| Refractoriness | 1700-1800℃ |
| Name | Magnesia Chrome Brick |
| Linear Change | ≤0.4% |
| Bulk Density | 2.7-3.0 G/cm3 |
CH Refractories Magnesia Chrome Brick (Model Number: CH-N) is a heat-resistant material, with a refractoriness of 1700-1800℃ and linear change of ≤0.4%, which makes it an ideal choice for applications requiring furnace mgo bricks. Additionally, its corrosion resistance is good, and its apparent porosity and porosity are both ≤18% and ≤22% respectively.
These magnesite chrome bricks are mainly used for high temperature furnaces, such as glass kiln, ceramic kiln, annealing furnace, and other industrial furnaces. Furthermore, these mgo bricks have excellent thermal shock and abrasion resistance, and are able to withstand long-term use in high-temperature environments.
CH Refractories Magnesia Chrome Bricks are a great choice for industries such as metallurgy, ceramics, glass, and chemical engineering, in which high temperature furnaces are used.
Brand Name: CH Refractories
Model Number: CH-N
Place of Origin: China
Cold Crushing Strength: ≥50 MPa
Name: Magnesia Chrome Brick
Refractoriness: 1700-1800℃
Porosity: ≤22%
Thermal Expansion Coefficient: 2.5-3.5×10-6/℃
We provide technical support and services for Magnesia Chrome Brick. Our technical support includes but not limited to: