Product Name: | Fire Brick | Size: | Customized |
---|---|---|---|
Application: | High Temperature Kiln And Furnace | Package: | Pallet |
Working Temperature: | More Than 1700 Degree |
This series of high temperature kiln refractory high alumina bricks use special grade aluminum bauxite clinker as the main raw material, supplemented by special additives, high pressure forming and high temperature firing. Refractory bricks alumina has the characteristics of large heat storage capacity and small creep rate.
The high alumina brick made by CH refractories with very widely application and various size with free mold charge to meet different kiln applications. To be professional high alumina furnace brick manufacturer since 1984, CH refractories provides alumina lining bricks not only can design fire furnace bricks size according to your kiln or furnace drawing for free, but also suggest you the most economical refractory furnace alumina bricks price for your kiln or furnace. Generally , there are three levels lime kiln refractory high alumina brick in our plant, just please inform bricks working condition, CH refractories will suggest you the most suitable alumina refractory bricks to save your money and achieve the best performance.
Applications of High Alumina Brick:
High alumina brick is widely used in the following refractory products:
●Coke oven
●Reheating furnace
●Steel smelting furnace
●Hot Blast Stove and boiler
●Blast furnaces and carbon furnace
●Cement kiln, glass kiln and tunnel kiln
●Steel ladle lining and various kiln lining
Advantages of CH series High Alumina Brick:
●low creep rate
●Large heat storage capacity
●Customerize mould according to different size requirements for free
●high strength,good thermal shock resistance,anti-stripping,Free sample,Free construction guidance ,free 3D design
Items | Index | |||
/ | CH-LZ75 | CH-LZ65 | CH-LZ55 | CH-LZ48 |
Al2O3%≥ | 75 | 65 | 55 | 48+ |
CCS/Mpa ≥ | 54 | 49 | 44 | 40 |
Apparent porosity/% ≤ | 23 | 23 | 22 | 22 |
Refractoriness under load /℃ ≥ | 1520 | 1500 | 1470 | 1420 |
Reheating linear change(1500℃,2h) | +0.1 -0.4 | +0.1 -0.4 | +0.1 -0.4 | +0.1 -0.4(1450℃.2h) |
Refractoriness/℃≥ | 1790 | 1790 | 1770 | 1750 |